Patent attributes
A method of preparing a hydrated calcium silicate (C—S—H) nano-film. The method includes: 1) synthesizing a hydrated calcium silicate powder having a calcium to silicon ratio (Ca/Si) of 0.5-3.0; 2) calcining the C—S—H powder obtained in 1) for 2-3 hours under a temperature of 150-250° C., cooling to approximately 25° C., and pressing the C—S—H powder under a pressure of 100-200 megapascal, to yield a target material; 3) fixing a substrate on a sample table of a magnetron sputtering apparatus, placing the target material obtained in 2) in a target position of the magnetron sputtering apparatus, pre-sputtering the target material for 5-10 minutes, rotating the substrate at a constant speed, sputtering the target material for 30-300 minutes, to yield a nano-film; and 4) soaking the nano-film obtained in 3) into in a saturated aqueous solution of calcium hydroxide at approximately 25° C. for 1-3 days.