Patent abstract
There are provided glass-ceramics comprising, in mass %, 50-60% SiO2, 22-26% Al2O3 and 3-5% Li2O, having an average crystal grain diameter exceeding 100 nm, and having an average linear thermal expansion coefficient of 30×10−7/° C. or below within a temperature range of 0° C. to 50° C. These glass-ceramics are manufactured by a step of melting glass raw materials, a step of forming the molten glass, a step of annealing the formed glass, a first heat treating step for heat treating the annealed glass at a temperature of 650-750° C. for 0.1 hour to 200 hours, and a second heat treating step for heat treating the glass at a temperature of 800-1000° C. for 0.1 hour to 50 hours.